Intruduction

Sinton’s silicon nitride igniters are normally rectangular in shape. These igniters have a lot operation zone up to 1000 degree C . and a cold zone in the contact area. Encapsulated terminal can prevent short circuit caused by conductive contamination. They can be operated with or without a controller. Silicon nitride igniters have several times the durability than that of silicon carbide products.

Dimension , power and input voltage are customizable according to your requirement.

Silicon Nitride igniter can heating up to 800 to 1000degree within tens of seconds. Silicone Nitride ceramic can sustain corrosion of melting metals. With proper instatllation and igniting process , the igniter can server several years.

Advantage

Fast Heating up

Corrosion resistance 

Long service life

Application

1. Ignition of solid fuels(eg wood pellets)

2. Ignition of gas or oil

3. Reburning or igniter of exhause fumes

4. Heating of process gases

5. Pyrotechnics

6. Brazing machines

7. Heater for corrosive atmosphere

8. R&D – laboratory equipment , measuring and testing equipment , reactors

9. Mold , tool heating

10. Charcoal barbecue grill

Test report

Physical and Chemical Properties of Silicon Nitride

Bulk Density 3.2-3.3g/cm3

Relative Density %  99-100%

Fracture Toughness  5.0-8.0 MPa*m1/2

Bending Strength(RT)    higher than 800 MPa

Bending strength (HT)      higher than 600 MPa

Vickers Hardness     15-20 GPa

Relative Dielectric Constant   6-7

Volume Resistivity   1014 ohm*cm

Thermal Conductivity   40-50 W/(m*K)

Thermal Expansion Coefficient    3.0 x 10 -6 /K

Acid Corrosion Resistance     Corrosion Rate less than 10g/m2*h after 6 h in 5% sulfuric acid boiling solution

Alkali Corrosion Resistance  Corrosion rate less than 0.6g/m2*h after 6 h in 30% sodium hydroxide boiling solution

Three point bending strength under 800 C degree

The Values is the test result under 10kg load